    Default Moisture content for Canoe Stems - Cellery Top Pine.

    Hello,

    I'm in the process of starting a cedar strip 18' Prospector, will be using Western Red for the strips and Cellery Top for the stems, seats, inwhales etc.

    Having purchased some many years old outdoor seasoned planks of Cellery I'm told the moisture content measured at 14%, is this too damp for laminating the stems? I understand for furniture I should be aiming for around 10 - 12 %, I wonder if slightly higher would be an advantage for bending?

    Any advice would be appreciated?

    Roy.

  2. # ADS
    Google Adsense Advertisement
    Join Date
    Always
    Location
    Advertising world
    Posts
    Many





     
  3. #2
    Join Date
    Aug 2015
    Location
    United States
    Posts
    318

    Default

    Quote Originally Posted by Plane sailing View Post
    Hello,

    I'm in the process of starting a cedar strip 18' Prospector, will be using Western Red for the strips and Cellery Top for the stems, seats, inwhales etc.

    Having purchased some many years old outdoor seasoned planks of Cellery I'm told the moisture content measured at 14%, is this too damp for laminating the stems? I understand for furniture I should be aiming for around 10 - 12 %, I wonder if slightly higher would be an advantage for bending?

    Any advice would be appreciated?

    Roy.
    I don't think you'll have ant troubles When I built My boat I used pine and Titebond III; But if you concerned use epoxy resin or Cascophen this is the glue in Marine grade ply.
    How ever this is not easy to find here in the States I'm not sure you can get it down under, this is where I buy it.
    http://www.aircraftspruce.com/catalo...?clickkey=3807

    Your stem will still be exposed to air for a good bit as you glue up your strips to help it dry some more and finish the out side of the canoe; Make sure to get REAL BRASS -BRONZE nails to hold your strips to the stem.

    I saw your post on my build thread; Good luck w/ yours I'll be looking in I hope you show your build progress.

    Bruce

  4. #3
    Join Date
    Feb 2008
    Location
    Eustis, FL, USA
    Posts
    2,270

    Default

    If using epoxy, this is on the high side, but on a technical level, anything below 15% will do, it's just there's no margin of error and this is why the formulators recommend 12%. This is also because they know some small amount of moisture gain is possible, even with the epoxy coating, so they leave a error margin, below where rot and other issues usually begin (about 17%). Simply put, if the moisture content is 12% and you do gain a few percent, with an immersed piece, you'll still be safe, but if you start with 14% - 15%, a couple more percent will push the piece into the danger zone.

    Bending is best down with heat and moisture content. It's the heat that does the work, but a higher moisture content will help prevent some breakage. You're going to have some breakage, even with the best stock. On strips I just use a heat gun, screw the steam box. If the stock is especially dry, I'll soak it, but it's the heat that does the work.

    Don't use brass fasteners or hardware, unless it's decorative and not going to get wet much. Bronze and stainless are the usual preferred choices.

    Cascophen is just resorcinol (phenol formaldehyde) and though there are several formulations, the plywood industry mostly uses heat activated melamine adhesives, though some phenols are still used, these too are typically cured with temperatures, while Cascophen is commonly room temperature cured.

  5. #4
    Join Date
    Mar 2007
    Location
    Hobart, Tasmania
    Posts
    24

    Default

    Quote Originally Posted by PAR View Post
    If using epoxy, this is on the high side, but on a technical level, anything below 15% will do, it's just there's no margin of error and this is why the formulators recommend 12%. This is also because they know some small amount of moisture gain is possible, even with the epoxy coating, so they leave a error margin, below where rot and other issues usually begin (about 17%). Simply put, if the moisture content is 12% and you do gain a few percent, with an immersed piece, you'll still be safe, but if you start with 14% - 15%, a couple more percent will push the piece into the danger zone.

    Bending is best down with heat and moisture content. It's the heat that does the work, but a higher moisture content will help prevent some breakage. You're going to have some breakage, even with the best stock. On strips I just use a heat gun, screw the steam box. If the stock is especially dry, I'll soak it, but it's the heat that does the work.

    Don't use brass fasteners or hardware, unless it's decorative and not going to get wet much. Bronze and stainless are the usual preferred choices.

    Cascophen is just resorcinol (phenol formaldehyde) and though there are several formulations, the plywood industry mostly uses heat activated melamine adhesives, though some phenols are still used, these too are typically cured with temperatures, while Cascophen is commonly room temperature cured.

    Thanks for the wonderful advice, I'm using Titebond III for the stems.
    I decided they are wholly encased in glass towards the end of the project so there is a bit
    more time for the moisture to make its escape.
    Bending went surprisingly well, I did experiment with different thickness strips until I
    was happy with the ease of bending without looking too spindly. Just a bit of patience is all it
    took (and another pair of hands to put the clamps on). It's all dry clamped
    for a little time, just to make glue up a little easier.

    My main issue at present is air temperature, or lack thereof, Titebond suggests a minimum temp of 45f or 8C.
    Being in Tasmania it's just a bit too cold ambient in the workshop for me to be comfortable. I'm uncertain if the
    lower end of the scale for the Titebond is just a guide and all I need to do
    is clamp for a few days longer or is there something a little more sinister with
    the activation/cure at lower temps. It talks about something called "Chalking point" associated with the lower
    temp. A bit more reading is needed.

    Ok here we go, straight from Titebond tech info:

    Chalk Temperature

    When glue dries, the loss of water pulls the adhesive particles together with

    enough force to form a continuous film. If the drying temperature is below a
    critical point, water evaporation is not sufficient to pull the particles together,
    leaving them in the joint. The dried film in the joint will appear whiter than
    normal. This is known as "chalking" and the critical temperature is the "chalk

    temperature." When chalking occurs, the glued joint loses strength and could

    result in a failed bond.



    I wasn't planning on using a brass protection strip on the bow/stern - my thoughts are so much time
    is spent encasing the stems, why would you go drilling a hole into it and compromise this.
    At this stage my plan is to epoxy the seats to a block on the hull rather than bolt/hang from the inwhales.

    Cheers for the awesome response.
    Roy.

  6. #5
    Join Date
    Apr 2008
    Location
    Tuross Head, South Coast, NSW
    Age
    77
    Posts
    155

    Default

    Quote Originally Posted by Plane sailing View Post

    My main issue at present is air temperature, or lack thereof, Titebond suggests a minimum temp of 45f or 8C.
    Being in Tasmania it's just a bit too cold ambient in the workshop for me to be comfortable. I'm uncertain if the
    lower end of the scale for the Titebond is just a guide and all I need to do
    is clamp for a few days longer or is there something a little more sinister with
    the activation/cure at lower temps. It talks about something called "Chalking point" associated with the lower temp.

    Cheers for the awesome response.
    Roy.
    I had an issue with chalking when I was building a strip built kayak and the temperature was about 4 degrees C.
    I tried warming the glue joint with the heat gun. It took just a couple of seconds for the chalkiness to disappear and even though temperature remained well below 8 degrees, the glue then seemed to continue to set.
    It didn't seem to affect the strength, but as it was only a strip kayak, the glue joint didn't need to be particularly strong.
    It seemed as if just a couple of seconds of warming was enough to get rid of the chalky appearance and kick start the reaction.

  7. #6
    Join Date
    Mar 2007
    Location
    Hobart, Tasmania
    Posts
    24

    Default

    Once again, thanks for the advice, the more I read the more I have decided it's just going to be sensible to run the fan heater in the workshop for 24hrs or so to keep the ambient temp well above 8C and be happy that I get a sound cure. Its probably warmer than that anyway. Heating may have worked for the strips, for a large volume like the stems I'm just not prepared to risk it.

    Cheers,

    Roy.

  8. #7
    Join Date
    Feb 2008
    Location
    Eustis, FL, USA
    Posts
    2,270

    Default

    I'm fortunate in that it's very rare for me to need a heater, just to get a cure, but in our winter, it happens occasionally enough that I bought a few of the hot oil filled heaters. Toss them under a tarp with the work and let them warm everything up. PVA's don't need to be at 45 degrees for the whole cure, just the first portion, until it's no longer tacky (an hour or so). It'll still need to have sufficient temperature to fully cure, but 80% of it is done in the first hour or two. This is usually enough to let the full cure wait until it warms up a bit the following day (roll her out into the sun and put a dark tarp over it).

  9. #8
    Join Date
    Mar 2007
    Location
    Hobart, Tasmania
    Posts
    24

    Default

    Quote Originally Posted by PAR View Post
    I'm fortunate in that it's very rare for me to need a heater, just to get a cure, but in our winter, it happens occasionally enough that I bought a few of the hot oil filled heaters. Toss them under a tarp with the work and let them warm everything up. PVA's don't need to be at 45 degrees for the whole cure, just the first portion, until it's no longer tacky (an hour or so). It'll still need to have sufficient temperature to fully cure, but 80% of it is done in the first hour or two. This is usually enough to let the full cure wait until it warms up a bit the following day (roll her out into the sun and put a dark tarp over it).
    Cheers,
    ill run the fan heater in the workshop and might take the laminates into my house to warm up the bulk of the timber and of course warming the glue prior to gluing. Once the workshop is warm I should be fine with the cure.

    roy

Similar Threads

  1. Assessing moisture content via weight
    By woodbe in forum TIMBER
    Replies: 10
    Last Post: 7th April 2012, 05:15 PM
  2. Moisture content
    By Islander in forum WOODTURNING - GENERAL
    Replies: 3
    Last Post: 16th October 2010, 08:45 PM
  3. Acceptable moisture content
    By Bodgy in forum SMALL TIMBER MILLING
    Replies: 15
    Last Post: 21st August 2008, 11:02 PM
  4. moisture content
    By coffenup in forum WOODTURNING - GENERAL
    Replies: 6
    Last Post: 26th June 2008, 11:35 PM
  5. Moisture Content Meter
    By Mick4412 in forum TIMBER
    Replies: 16
    Last Post: 15th September 2004, 03:11 AM

Posting Permissions

  • You may not post new threads
  • You may not post replies
  • You may not post attachments
  • You may not edit your posts
  •