19th October 2014, 08:38 PM #1
West Systems Epoxy and Schweppervescence
When mixing up common West Systems epoxy at work (one even dose via pump bottles) I always get tiny little bubbles appearing in the mix container (a small tunafish tin). These bubbles then obviously end up in the work piece, and while some amalgamate into bigger surface bubbles that can be popped before curing, there always seems to be a little bit of "fizz" left behind in the cavity (ie: small holes like bird's eyes and/or bigger "tears").
Am I expecting too much wanting a completely solid mix, or am I doing something wrong?
I've tried changing the way I mix with smaller/bigger stirring sticks and by stirring less vigorously but I can't for the life of me stop "introducing" these little bubbles at the mixing stage.
The teeny bubbles don't stand out *too* much when fully cured, and I know that customers haven't seen them, but I know the blighters are there and it's messing with my OCDEvery time you make a typo, the errorists win.
-
19th October 2014 08:38 PM # ADSGoogle Adsense Advertisement
- Join Date
- Always
- Location
- Advertising world
- Age
- 2010
- Posts
- Many
-
19th October 2014, 09:38 PM #2
Did someone once say advertising doesn't work? You even got the complex spelling spot on!
-
19th October 2014, 09:39 PM #3
Lol...I admit, I had to Google it first...remember...OCD
Every time you make a typo, the errorists win.
-
19th October 2014, 09:43 PM #4Senior Member
- Join Date
- Apr 2012
- Location
- Melbourne
- Posts
- 292
hi reshirtguy..
the bubbles are also caused by chemical reaction during the process of hardening...
As you will see when epoxy cures it emits heat.. as well as some gases...
when using some epoxies you can pop bubbles by going quickly and lightly with the flame torch over them...
I haven't tried that on the western system though.. i guess next time someone uses western system, can try on a bit of excess and advise whether the flame torch works on bubble popping...
Otherwise.. another technique is to pour it a bit thin giving more time for bubbles to surface... also doing it in multiple goes so it is not too deep....
I've used it few times to fill knot holes and ended up with minimum to none of the bubbles captured by pouring it while it is still very runny...
and then spend extended time continuously popping surface bubbles (lets say I've spent about an hour popping bubbles)
Alen
-
19th October 2014, 09:44 PM #5
heh heh, Shweps don't care if you're OCD, can't spell, or both and perhaps more, just keep drinking....
Now what's the bet that the next time you're in the supermarket or servo looking for a drink.........c'mon, you owe them at least one.
-
19th October 2014, 10:08 PM #6
Vacuum degas if you have the equipment. If not, try pouring it out from further up (like 200mm) in a thinner stream.
-
19th October 2014, 11:31 PM #7
-
20th October 2014, 06:46 PM #8
In a previous job we used to work with various types of epoxies, building military equipment. After mixing they would always be put in a vacuum chamber. We would pull a vacuum & the epoxy would turn to foam as the air came out. Quite often we would have to pull a vacuum & release it several times to collapse the foam to get all the air out.
One other thing we learnt, the hard way, is to keep any uncured silicons well away, as they can migrate through the air & can effect the strength & bonding of other epoxies & glues. After someone, who shall remain nameless , put a 2 part silicon mix in the vacuum chamber in one of the critical epoxy process areas, all silicon use was confined to one room in a building at the far end of the site & that room & everything in it had to be scrubbed with solvents to remove the silicon residue.
-
20th October 2014, 06:46 PM #9
In the mix container. Combine, mix, degas, use.
-
20th October 2014, 07:52 PM #10
Thanks folks. A few ideas to try
Most of the time I'm only filling little things like cracked knots or bird's eye and have been pressing the mix into the gap with a spatula to make sure it's in deep and leaving a small mound to sand off later. Any teeny little bubbles in those situations don't bother me *too* much, but it's the bigger tears and deep/wide cavities that have been bugging me (although they still look good enough to send out).
A vaccuum press is a bit too fancy for the amount of work we do with epoxy, but I'll give the thinner pouring and a bit of blowtorching a spin next time and see how it goes.
Ta muchlyEvery time you make a typo, the errorists win.
-
27th October 2014, 07:53 PM #11Senior Member
- Join Date
- Feb 2012
- Location
- Sydney
- Posts
- 187
The two tricks I've learnt are heat gun/blowtorch to warm up and thin the epoxy.
And the other is spraying to epoxy surface with mold release. This breaks the surface tension allowing any bubbles to pop.
-
28th October 2014, 05:52 AM #12GOLD MEMBER
- Join Date
- Apr 2011
- Location
- McBride BC Canada
- Posts
- 3,543
As 62woolybugger describes, air gets into the epoxy from the original components
and from the stirring/mixing process. Degassing several times in a vacuum chamber seems to
be the sole cure for it.
I don't agree that gasses are released during the cross linking polymerization process.
Otherwise I should have expected to see all of my biological research specimens
ruined. Not the case. 3+ years of as much as 30,000X in an electron microscope
showed no bubbles.
-
8th November 2014, 09:03 PM #13
As it happens I had some cracks and holes to fill with epoxy today in some recycled timber, so I thought I'd trying the vacuum process. I happen to have an Orved v12 Vac-Pack machine (can't sell the damn thing - maybe I don't want to now ). Gave the mix 6-8 good long runs in the vac and it certainly removed most of the bubbles - just a few very small ones that probably won't be noticeable.
Thanks to Master Splinter (again) for the tip.
After the first second or so of the vac process I could see the chamber get filled with a smoky vapour - not dense, but certainly easily visible. What the hell could that be I wonder?
I didn't think to do the vac with the first batch today, and so i hit the epoxy (already in the holes) with a small butane torch. It looks to have made the bubbles come up above the timber line so they can be sanded out, but tomorrow will reveal the truth.
If the epoxy is going white around the edges under the butane torch is that a sign of too much heat?
-
10th November 2014, 07:07 PM #14
It can be - but it can also be water vapour condensing out of the flame envelope onto the colder epoxy.
But the reaction can kinda' get away from you, as the hot epoxy reacts faster when warmed and can then exotherm, increasing its temperature even more.
(Rule of thumb is that a chemical reaction doubles in speed for every 10 degree increase in temperature).
-
10th November 2014, 07:14 PM #15
Cheers MS. As I thought, the bubbles have risen to above the timber line, and so were virtually all gone after I sanded back.
Interestingly, the epoxy mixed with Saw dust was significantly harder after the same time than the clear epoxy with no dust which was still quite sticky.
Similar Threads
-
Repair of epoxy on timber joint - epoxy to epoxy?
By bcp in forum GLUEReplies: 3Last Post: 3rd September 2014, 09:54 AM -
West Systems 2-part Epoxy Resin - Removing Bubbles
By cjkennedy99 in forum FINISHINGReplies: 7Last Post: 26th March 2011, 10:51 PM -
Epoxy: Techniglue Versus West Systems
By thumbsucker in forum WOODWORK - GENERALReplies: 16Last Post: 23rd June 2007, 01:44 PM -
West Systems HELP Please
By Quokka in forum WOODWORK - GENERALReplies: 11Last Post: 27th January 2006, 12:31 PM -
Epoxy supplier west side of Melb GPO
By Banjo in forum BOAT RESOURCES / PRODUCT SEARCHReplies: 4Last Post: 5th June 2004, 08:06 AM