    Default epoxy resin

    G'day all
    I've gone down the epoxy resin road for filling knots gum veins etc and also for glueing boards together for table tops as this method eliminates joint creep , I was hoping to hear from other forum members on there prefered method for applying epoxy resin ,I had a little trial run with the west 105 &207 clear hardener all went well but I thought it would have cured alot faster than it did all I can put it down to is the cold weather ???, anyone with some good info please fell free to comment.
    cheers osage...

  2. # ADS
    Google Adsense Advertisement
    Join Date
    Always
    Location
    Advertising world
    Posts
    Many





     
  3. #2
    Join Date
    Dec 2005
    Location
    Canberra
    Posts
    3,260

    Default

    Yes it's affected by the temperature - you can warm it up with a hair drier if you want to coax the cure along.

    If it's not solid after two days, you did something wrong (most likely resin/hardener ratios, which should be mixed accurately and not by 'near enough' - 5:1 by weight or volume for 205 or 206 BUT for 207 its 3.5:1 by weight or 3:1 by volume) so you get to learn how messy it is to remove gluggy epoxy....

    And mix for a good minute or two!

  4. #3
    Join Date
    Feb 2014
    Location
    Caroline springs
    Posts
    52

    Default

    Cheers ms yep the epoxy is rock solid so I guess my mix was ok I've also heard putting the containers in a bucket of warm water helps aswell I also left a bit in the measuring cup to see what colour it hardened to,very yellowish is there any other product that dries totally clear?

  5. #4
    Join Date
    Nov 2007
    Location
    Albury Well Just Outside
    Posts
    13,315

    Default

    I have also used epoxy as a gap filler with some black dye. One tip that I will share is not to over fill as it can take a while to flatten. I ended up using a scraper with very light touch then sand paper.

    I have also used casting resin for some turned bowls only one with no colour it was clear or clear-ish.

  6. #5
    Join Date
    Apr 2002
    Location
    Brisbane
    Posts
    5,773

    Default

    The thing to remember about all the modern marine epoxies is.....they are nothing like retail epoxies...thank goodness.

    They are intentionally slow curing..this give time when working with larger pieces.

    Start laying up meters of glass mat or sheets of laminate and you will be glad the stuff cures slowly.

    If the cure speed is a problem either way, there are slower and faster acting hardeners...never change the mix ratio....this is epoxy not any other type of resin...the mix ration is fixed regardless.

    If you are using it as glue or filler remember you need to add some sort of thickning agent or filler.....there is a wide choice.

    cheers
    Any thing with sharp teeth eats meat.
    Most powertools have sharp teeth.
    People are made of meat.
    Abrasives can be just as dangerous as a blade.....and 10 times more painfull.

Similar Threads

  1. EPOXY (HIGH CLARITY) RESIN + HARDENDER (2:1 RATIO)EPOXY
    By Lyle in forum WOODTURNING - GENERAL
    Replies: 8
    Last Post: 9th May 2014, 06:48 PM
  2. Epoxy resin
    By hellofellow in forum FINISHING
    Replies: 4
    Last Post: 1st May 2014, 07:04 PM
  3. looking for help with resin/ epoxy
    By gunny0369 in forum WOODTURNING - GENERAL
    Replies: 7
    Last Post: 12th March 2013, 05:47 PM
  4. Epoxy resin not curing
    By jaytendo in forum FINISHING
    Replies: 6
    Last Post: 13th November 2012, 09:24 AM
  5. Epoxy resin
    By kiwioutdoors in forum BOAT DESIGNS / PLANS
    Replies: 9
    Last Post: 29th May 2007, 11:54 PM

Tags for this Thread

Posting Permissions

  • You may not post new threads
  • You may not post replies
  • You may not post attachments
  • You may not edit your posts
  •